Micromechanical properties of veneer luting resins after curing through ceramics

The aim of this study was to assess the performance of light-cured luting resin after curing under the ceramic restoration in comparison to dual-cured luting resin, by evaluating the micromechanical properties. Two hundred seventy thin luting composite films of ca. 170 ىm in thickness were prepared by using two light-cured luting resins (Variolink Veneer, Ivoclar Vivadent; RelyX Veneer, 3M ESPE) and a dual-cured luting resin (Variolink II, Ivoclar Vivadent). The composites were cured by using a LED-unit (Bluephase®, Ivoclar Vivadent) with three different curing times (10, 20, and 30 s) under two ceramics (IPS e.max Press, Ivoclar Vivadent; IPS Empress® CAD, Ivoclar Vivadent) of different thicknesses (0, 0.75, and 2 mm). Forty-five groups were included, each containing six thin films. The samples were stored after curing for 24 h at 37°C by maintaining moisture conditions with distilled water. Micromechanical properties of the composites were measured with an automatic microhardness indenter (Fisherscope H100C, Germany). For each sample, ten indentations were made, thus totalizing 60 measurements per group. Micromechanical properties of the luting resins were statistically analyzed (SPSS 17.0). Significant differences were observed between the micromechanical properties of the luting resins (p<0.05). Variolink II showed the highest values in modulus of elasticity (E=11±0.5)* and Vickers hardness (HV=48.2± 3.2)* and the lowest values in creep (Cr=4.3±0.1)* and elastic–plastic deformation (We/Wtot=38.6±0.7)* followed by RelyX Veneer (E=6.9±0.3, HV=33±2.5, Cr=4.6±0.2, We/Wtot=41.8±1.0)* and Variolink Veneer (E=4.4±0.4, HV=20.1±2.6, Cr=5±0.2, We/Wtot=43.7±1.3)*. Dualcured luting resin expressed higher values in the micromechanical properties compared to the light-cured luting resins. The effect of luting resin type on the micromechanical properties of the luting resins was higher than the effect of curing time, ceramic type and ceramic thickness respectively (*The values of reference without ceramics for 30 s curing time).